Ceramic Fiber Blanket
-
Place of Origin:China
-
Minimum order:1
Ceramic Fiber Blanket is made of special ceramic long-fiber that is produced by the melting of very pure raw materials in double surface meeding process without binders and with good
stability in a large range of temperature.
The process of double surface needing increase interweaving and tensile strength. Ceramic fiber blanket is a needled blanket that has exceptional handling strength, while being flexible and
lightweight. Ceramic Fiber Blanket is made of high purity Alumino-Silicate (and Zirconia) fibrous wool.
Ceramic Fiber Blanket Characteristic:
--Needled blanket
--Non-combustible
--Low thermal conductivity
--Shorter heat up and cool down time
--Resilience and resistance to thermal shock
--Flexible and easy to cut or install
--Consist of acoustic properties
--Contain no organic binder
--Asbestos free--Excellent thermal stability
--Excellent chemistry quality
--Resistance to burning
--Low thermal capacity
--Good insulation
--Good obstructing voice and mechanism strength
--Low shrinkage
--Good springiness for fibers
--Convenient producing and installing
Ceramic Fiber Blanket Standard Size:
Available size(mm/roll)
Length: 3600mm, 7200mm
Width: 600mm, 610mm
Thickness: 20mm, 25mm, 50mm
Note: Other sizes could be customized as your request.
Ceramic Fiber Blanket Types
Item
|
JK-1100
|
JK-1260
|
JK-1420
|
JK-1600
|
Classification Temp(C)
|
1100
|
1260
|
1420
|
1600
|
Color
|
Pure White
|
Pure White
|
Pure White
|
Pure White
|
Density(kg/m3)
|
64
|
64
|
96
|
128
|
160
|
160
|
160
|
160
|
Permanent Linear Shrinkage(%) 24hours,128kg/m3
|
-3(1000C)
|
-3(1200C)
|
-3(1300C)
|
-3(1400C)
|
Thermal Conductivity(W/m.k) (128kg/m3)
|
0.09(400C)
|
0.09(400C)
|
0.12(600C)
|
0.16(800C)
|
0.16(800C)
|
0.16(800C)
|
0.2(1000C)
|
0.2(1000C)
|
Tensile Strength(Mpa),128kg/m3
|
0.08-0.12
|
0.08-0.12
|
0.08-0.12
|
0.08-0.12
|
Chemical Composition (%)
|
Al2O3
|
46
|
47-49
|
52-55
|
39-40
|
Al2O3+SiO2
|
97
|
99
|
99
|
-
|
ZrO2
|
-
|
-
|
-
|
15-17
|
Fe2O3
|
<1.0
|
0.2
|
0.2
|
0.2
|
Na2O+K2O
|
≤0.5
|
0.2
|
0.2
|
0.2
|
Note: Data are average results of standard tests which are subject to variation and should not be used as specification
Ceramic Fiber Blanket Application:
--Refractory back-up installation
--Direct exposure to heat as furnace hot face lining
--Expansion joint seal
--Fire protection
--General high temperature insulation
--Lining for furnaces, kiln and oven
--Expansion joints and seals for furnace, kiln and oven
--Back-up installation
--Lagging of high temperature pipe work
--High temperature filtration
--Steam turbine and nuclear insulation
--Fire protection
International Enterprises Center, No. 72, Nongye Rd., Jinshui District, Zhengzhou, Henan, China
Tel: 86-371-63355891 Fax: 86 371 63355893
Country: China (Mainland)