Model Number: | LIM1580AB |
Brand Name: | SQUARE |
Place of Origin: | Guangdong, China |
9. Remarks These figures are for reference only,Please contact us for detail.
Cure condition: 7 min*150
Mixing ratio of AB=11
16.6
24.0
kN/m
ASTM D624 Die B
Tear strength
252
360
%
DIN53504 S2
Elongation
6.45
7.2
mpa
DIN53 504 S2
Tensile strength
75
70
Shore A
DIN53 305
Hardness, Shore A
550
550
Pa.s
Viscosity
LIM1580A/B
LIM1570A/B
Unit
Standard
Item 8. Product data Correctly stored in its original closed container at room temperature (max 27). SQUARE?LIM1580A/B has a shelf life of 360 days. The ready to use LIM1580A/B should be kept tightly closed and used up within 7 days. 7. Storage SQUARE?LIM1580A/B is available in 20kgs pails and 200kgs drums. 6. packaging 5. How to use: Ready-to-use mixturescomponent A and Bare fed directly to injection molding machine from the original containers by means of a metering end mixing unit called static mixer. The mixtureat the mixing ratio 11 is injected into the heated mould at the mould temperature of 160-200,the mixed silicone rubber will be vulcanized in a few seconds. 4. ApplicationSQUARE?LIM1570A/B1580A/B is suitable for making P+R cellphone keypad etc . (7) Fast curing under high temperature (6) Outstanding resistance to ageing (5) Low shrinkage (4) Low yellowing (3) Excellent thermal and cold stability (2) Good rebound property (1) High tear strength |
High tear strength
Good rebound property
Low yellowing
SiSiB® HR0100 is general purpose heat cured elastomer for molding. Technical Data Product HR0130 HR0140 HR0150 Appearance Translucent Translucent Translucent Hardness (Shore A) 30+/-2 40+/-2 50+/-2 Williams Plasticity 130+/-20 160+/-20 215+/-24 Tensile Strength (MPa) Min. 4.0 ...
1.Material and Hardness:LSR 55-60A fog face and transparent 2.Counterpart:/ 3.Packaging:/ Dongguan JuYan Silicone Technology Co.,Ltd (a BELLO company) is dedicated to offer high-quality rubber &silicone parts by integrating R&D,production,sales and service ,which are widely ...
Model Color Mixing ratio Pot life (mins) Demouled time (hrs) Hardness(A0) Tensile-strength (kgf/cm2) Tear-strength (kgf/cm) Viscosity (cps) Elongation (%) HY-E625 translucent 1 : 1 30-60 4±1 25±2 35±2 25±2 6000±3000 ≥400 HY-E630 translucent 1 : 1 30-60 4±1 30±2 40±2 ...
HY-210can be applied to the sealing and pouring of various electronic components, and then forming insulation system with no corrosion and negligible shrinkage. HY-210is suitable for bonded seal of electronic components, power module and control module, LED invertor potting, ...
Tin cured mould making liquid silicone rubber for sell Product Description 1.Description of Tin cured mould making liquid silicone rubber for sell It\'s a kind of room temperature vulcanized silicone rubber in condensation type. It’s generally named as two part silicone ...
Description of liquid tin cure silicone rubber for small crafts mold making: HY-620 is a kind of room temperature vulcanized silicone rubber in condensation type. It’s generally named as two part silicone rubber , Part A is a flowable liquid, part B is the curing agent or ...
Prototyping is to make one or several products according to drawing , without making the mould. Prototype is mainly for checking the appearance or function before production.Usually when a product design finished, it needs to make the prototype. ...
Characteristics An exceptional fluidity and good operability, easy to demold Good tensile and tear strength Outstanding bubble releasing Non-deformation Low shrinkage Aging resistance ,high temperature resistance (200℃) Environmentally, food-grade Warm tips : 1.As ...
Features of Platinum cured silicone rubber for cake molding making: 1. Two-component silicone rubber, partA and partB 2. High transparency, tensile strength, and tear strength. 3. Nontoxic & reach to Food grade, skin-touch safe 4. Good heat stability and weather ...
Application Platinum cure molding rubber silicone rtv is used for prototyping and the reproduction of parts. Silicone moulds can be constructed in many different forms depending on the shape of the part you are making. In this section we will outline how to create the ...